Hot Deformation Behavior of Ni80A Superalloy During Non-Isothermal Side Pressing | ||
| Iranian Journal of Materials Forming | ||
| مقاله 3، دوره 2، شماره 1، تیر 2015، صفحه 18-29 اصل مقاله (1.25 M) | ||
| نوع مقاله: Research Paper | ||
| شناسه دیجیتال (DOI): 10.22099/ijmf.2015.2912 | ||
| نویسندگان | ||
| M. Seyed Salehi1؛ N. Anjabin* 2؛ R. Mansoori3 | ||
| 1Department of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran | ||
| 2Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran | ||
| 3Research and Development Center, Turbine Machine Middle East Co., Tehran, Iran | ||
| چکیده | ||
| In the present study, the microstructural changes of a Nickel based superalloy Nimonic 80A during a non-isothermal deformation were studied. Therefore, microstructure evolution during hot side pressing test was predicted with combined methods of finite element analysis and processing map of the material. The predicted results were validated through experimental microstructural studies. The results show that the distribution of deformation parameters (i.e. strain, strain rate, and temperature) is non-uniform in the deformed samples. The severity of this non-uniformity depends on the amount of sample reduction. High reduction value at one step forging can cause flow localization and non-uniform dynamic recrystallization, which results the formation of adiabatic shear bands, while using the lower reduction value at each forging step, leads to more uniformly distribution of the deformation parameters and thus uniform the dynamic recrystallization with the stable flow. Hence the workability and microstructure of the Nimonic 80A alloy are mainly depends on the deformation path. | ||
| کلیدواژهها | ||
| Hot deformation؛ Nimonic 80A؛ Processing map؛ Microstructure؛ Finite Element Analysis | ||
| مراجع | ||
|
[1] D. Bombac, M. T. Fazarinc and S. V. Goran Kugler, Microstructure development of Nimonic 80A superalloy during hot deformation, Materials and Geoenviroment, 55 (2008) 319-328.
[2] D. Bombac, M. Brojan, M. Tercelj and R. Turk, Response to hot deformation conditions and microstructure development of Nimonic *0A superalloy. Materials and Manufacturing Processes, 24 (2009), 644-648.
[3] S.Kargarnejad and F. Djavanroodi, Failure assessment of Nimonic 80A gas turbine blade. Engineering Failure Analysis, 26 (2012), 211-219.
[4] T.M. Pollock and S. Tin, Nickle-based superalloys for advanced turbine engines: chemistry, microstructure and properties. Journal of propulsion and power, 22(2) (2006), 361-374.
[5] G. Tai, Y. He and L. Yu-li, Backward tracing simulation of precision forging process for blade based on 3D FEM. Trans. Nonferrous Met. Soe. China, 16 (2006), 639-644.
[6] S. L. Semiatin and J. J. Jonas, Formability and workability of Metals, IV (1984), Ohio: American Society for Metals.
[7] G. E. Dieter, Evaluation of Workability. (1990), University of Maryland.
[8] A. R. Mashreghi, H. Monajatizadeh, M. Jahazi and S. Yue, High temperature deformation of nickel base superalloy Udimet 520. Materials Science and Technology, (2004), 161-166. [9] Z. M. Hu, J.W. Brooks and T.A. Dean, Experimental and theoretical analysis of deformation and microstructural evolution in the hot die forging of titanium alloy aerofoil sections. Journal of Materials Processing Technology, 88 (1999), 251-265. [10] R. S. Lee and H.C. Lin, Process design based on the deformation mechanism for the non-isothermal forging of Ti–6Al–4V alloy. Journal of Materials Processing Technology, 79 (1998), 224-235. [11]Y. Prasad and S. Sasidhara, Hot Working Guide: A Compendium of Processing Maps, (1997), ASM international. [12]L. U. Shi-qiang, L. Xin, K. L. Wang, L. Shi-biao and M. W. FU, A method for prediction of unstable deformation in hot forging process by simulation. Transactions of Nonferrous Metals Society of China, 23(12) (2013), 3739-3747. [13] N. Srinivasa and Y. Prasad, Hot working characteristics of nimonic 75, 80A and 90 superalloys: a comparison using processing maps. Journal of Materials Processing Technology, 51(1) (1995), 171-192. | ||
|
آمار تعداد مشاهده مقاله: 1,966 تعداد دریافت فایل اصل مقاله: 2,147 |
||