Hot Ductility Behavior of the Electrolytic Tough Pitch Copper Having Different Initial Oxygen Content | ||
| Iranian Journal of Materials Forming | ||
| دوره 9، شماره 4، دی 2022، صفحه 13-25 اصل مقاله (3.89 M) | ||
| نوع مقاله: Research Paper | ||
| شناسه دیجیتال (DOI): 10.22099/ijmf.2022.44143.1232 | ||
| نویسندگان | ||
| H.R. Abedi* 1؛ A. Zarei-Hanzaki* 2؛ Z. Loghman Nia3؛ M. Taherimandarjani4؛ A. Moshiri2 | ||
| 1School of Metallurgy & Materials Engineering, Iran University of Science and Technology (IUST), Tehran, Iran | ||
| 2School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran | ||
| 3Humboldt-Universität zu Berlin, Department of Chemistry, Brook-Taylor-Str. 2, 12489 Berlin, Germany | ||
| 4Department of Mechanical and Product Design Engineering, School of Engineering, Faculty of Science, Engineering and Technology, Swinburne University of Technology, Hawthorn, VIC, 3122, Australia | ||
| چکیده | ||
| The possible ductility troughs of tough pitch copper containing various oxygen contents were identified to determine the safe and unsafe thermomechanical processing domains. Tensile and compression tests were conducted in temperature range of 300-800°C. The critical strain of single/multiple peaks dynamic recrystallization decreased by increasing oxygen content up to 220 ppm, and again increased with further increment up to 390 ppm. The non-uniform elongation region increased by increasing the temperature, and above 500°C, it was the dominant portion of the tensile curves. The long post-uniform elongation was attributed to the occurrence of dynamic recrystallization which increased the resistance of the material to localized necking. Two ductility troughs (unsafe thermomechanical processing regions) were recognized at temperatures of 400±50°C and 600±50°C. The ductility drop regions shifted to lower temperatures with an increase in the strain rate. The variation of the oxygen content, however, did not have significant effects on the position of ductility drops. The current work also explores the fracture surface characteristics of the tensile tested specimens. | ||
| کلیدواژهها | ||
| Tough pitch copper؛ Ductility trough؛ Oxygen content؛ Thermomechanical processing | ||
| مراجع | ||
|
[1] B. Mintz, S. Yue, J.J. Jonas, Hot ductility of steels and its relationship to the problem of transverse cracking during continuous casting, International Materials Reviews, 36(1) (1991) 187-220.
[2] B. Mintz, The influence of composition on the hot ductility of steels and to the problem of transverse cracking, ISIJ international, 39(9) (1999) 833-855.
[3] I. Mejíaa, A. Bedolla-Jacuinde, C. Maldonado, J.M. Cabrera, Hot ductility behavior of a low carbon advanced high strength steel (AHSS) microalloyed with boron, Materials Science and Engineering: A, 528(13-14) (2011) 4468-4474.
[4] A. Haft Baradaran, A. Zarei-Hanzaki, H. Abedi, S. Fatemi-Varzaneh, A. Imandoust, The ductility behavior of a high-Mn twinning induced plasticity steel during cold-to-hot deformation, Materials Science and Engineering: A, 561 (2013) 411-418.
[5] A.S. Hamada, L.P. Karjalainen, Hot ductility behaviour of high-Mn TWIP steels, Materials Science and Engineering: A, 528(3) (2011), 1819-1827.
[6] R. Nowosielski, P. Sakiewicz, P. Gramatyka, The effect of ductility minimum temperature in CuNi25 alloy, Journal of Materials Processing Technology, 162 (2005) 379-384.
[7] W. Ozgowicz, The relationship between hot ductility and intergranular fracture in a CuSn6P alloy at elevated temperatures, Journal of Materials Processing Technology, 162 (2005) 392-401.
[8] M.H. Ghavam, M. Morakabati, S.M. Abbasi, H. Badri, Hot ductility behavior of near-alpha titanium alloy IMI834, International Journal of Materials Research, 105(11) (2014) 1090-1096.
[9] H.R. Abedi, A. Zarei-Hanzaki, S. Khoddam, Effect of γ precipitates on the cavitation behavior of wrought AZ31 magnesium alloy, Materials & Design, 32(4) (2011) 2181-2190.
[10] O. Sabokpa, A. Zarei-Hanzaki, H.R. Abedi, Mater, An investigation into the hot ductility behavior of AZ81 magnesium alloy, Materials Science and Engineering: A, 550 (2012) 31-38.
[11] M. Taheri-Mandarjani, A. Zarei-Hanzaki, H.R. Abedi, Hot ductility behavior of an extruded 7075 aluminum alloy. Materials Science and Engineering: A, 637 (2015) 107-122.
[12] W.L. Chan, M.W. Fu, J. Lu, J.G. Liu, Modeling of grain size effect on micro deformation behavior in micro-forming of pure copper, Materials Science and Engineering: A, 527(24-25) (2010) 6638-6648.
[13] W.L. Chan, M.W. Fu, B. Yang, Study of size effect in micro-extrusion process of pure copper, Materials & Design, 32(7) (2011) 3772-3782.
[14] B. Yang, C. Motz, M. Rester, G. Dehm, Yield stress influenced by the ratio of wire diameter to grain size–a competition between the effects of specimen microstructure and dimension in micro-sized polycrystalline copper wires, Philosophical Magazine, 92(25-27) (2012) 3243-3256.
[15] A.T. Jennings, M.J. Burek, J.R. Greer, Microstructure versus size: mechanical properties of electroplated single crystalline Cu nanopillars, Physical Review Letters, 104(13) (2010) 135503.
[16] J.Q. Su, T.W. Nelson, T.R. Mc Nelley, R.S. Mishra, Development of nano-crystalline structure in Cu during friction stir processing (FSP), Materials Science and Engineering: A, 528(16-17) (2011) 5458-5464.
[17] T. Sakai, H. Miura, X. Yang, Ultrafine grain formation in face centered cubic metals during severe plastic deformation, Materials Science and Engineering: A, 499(1-2) (2009) 2-6.
[18] K. Youssef, M. Sakaliyska, H. Bahmanpour, R. Scattergood, C. Koch, Effect of stacking fault energy on mechanical behavior of bulk nanocrystalline Cu and Cu alloys, Acta Materialia, 59(14) (2011) 5758-5764.
[19] X.Y. San, X.G. Liang, L.P. Chen, Z.L. Xia, X.K. Zhu, Influence of stacking fault energy on the mechanical properties in cold-rolling Cu and Cu–Ge alloys, Materials Science and Engineering: A, 528(27) (2011) 7867-7870.
[20] A. Belyakov, T. Sakai, H. Miura, K. Tsuzaki, Grain refinement in copper under large strain deformation, Philosophical Magazine A, 81(11) (2001) 2629-2643
[21] H. Khodaverdizadeh, A. Mahmoudi, A. Heidarzadeh, E. Nazari, Effect of friction stir welding (FSW) parameters on strain hardening behavior of pure copper joints, Materials & Design, 35 (2012) 330-334.
[22] F. Cao, I.J. Beyerlein, F.L. Addessio, B.H. Sencer, C.P. Trujillo, E.K. Cerreta, G.T. Gray III, Orientation dependence of shock-induced twinning and substructures in a copper bicrystal, Acta Materialia, 58(2) (2010) 549-559.
[23] H. Zhang, H.G. Zhang, D.S. Peng, Hot deformation behavior of KFC copper alloy during compression at elevated temperatures, Transactions of Nonferrous Metals Society of China, 16(3) (2006) 562-566.
[24] S.H. Huang, D.Y. Shu, C.K. Hu, S.F. Zhu, Effect of strain rate and deformation temperature on strain hardening and softening behavior of pure copper, Transactions of Nonferrous Metals Society of China, 26(4) (2016) 1044-1054.
[25] S. H. Huang, S.X. Chai, X.S. Xia, Q. Chen, D.Y. Shu, Compression deformation behaviour and processing map pf pure copper, Strength of Materials, 48 (2016) 98-106.
[26] A. Belyakov, H. Miura, T. Sakai, Dynamic recrystallization under warm deformation of polycrystalline copper, ISIJ International, 38(6) (1998) 595-601.
[27] M. Heinemann, B. Eifert, C. Heiliger, Band structure and phase stability of the copper oxides Cu2O, CuO, and Cu4O3, Physical Review B, 87(11) (2013) 115111.
[28] ASTM E21, Standard test methods for elevated temperature tension tests of metallic materials, ASTM International, 1988.
[29] ASTM E209, Standard practice for compression tests of metallic materials at elevated tmperatures with conventional or rapid heating rates and strain rates, ASTM International, 2010.
[30] F.J. Humphreys, M. Hatherly, Recrystallization and related annealing phenomena, Elsevier, 2004.
[31] P. Zhao, T.S.E. Low, Y. Wang, S.R. Niezgoda, An integrated full-field model of co-current plastic deformation and microstructure evolution: Application to 3D simulation of dynamic recrystallization in polycrystalline copper, International Journal of Plasticity, 80 (2016) 38-55.
[32] N. Ravichandran, Y.V.R.K. Prasad, Influence of oxygen on dynamic recrystallization during hot working of polycrystalline copper, Materials Science and Engineering: A, 156(2) (1992) 195-204.
[33] B.H. Chen, H. Yu, Hot ductility behavior of V-N and V-Nb microalloyed steels, International Journal of Minerals, Metallurgy, and Materials, 19(6) (2012) 525-529. | ||
|
آمار تعداد مشاهده مقاله: 219 تعداد دریافت فایل اصل مقاله: 217 |
||