Formation of a solid solution through accumulative roll bonding (ARB) and post-heat treatment of multilayered Cu/Zn/Al | ||
| Iranian Journal of Materials Forming | ||
| مقاله 3، دوره 1، شماره 1، تیر 2014، صفحه 24-31 اصل مقاله (860.35 K) | ||
| نوع مقاله: Research Paper | ||
| شناسه دیجیتال (DOI): 10.22099/ijmf.2014.2277 | ||
| نویسندگان | ||
| M. Reihanian* 1؛ M.M. Mahdavian2؛ L. Ghalandari3؛ A. Obeidavi2 | ||
| 1Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University, Ahvaz, Iran | ||
| 2Islamic Azad University, Ahvaz, Iran | ||
| 3Islamic Azad University, Shiraz, Iran | ||
| چکیده | ||
| In the present study, the capability of accumulative roll bonding (ARB) and subsequent heat-treatment to fabricate solid solution from a multilayered Cu/Zn/Al was investigated. Two post-heat treatment (one-step and two-step) routes were proposed. In the first, the ARB processed material was heated to 800 C for 5:30 hours and allowed to cool slowly in a furnace (one-step route). In the second (two-step route), the composite was heated to 800 C for 3 hours and quenched in the cold water (0 ºC). The microstructures were characterized using a field emission scanning electron microscope (SEM) equipped with energy dispersive x-ray detector (EDX). The x-ray diffraction (XRD) pattern was used to identify the phases. Results showed that even after imposing high ARB cycles (up to 14 cycles), the solid solution could not be formed so far. However, after the subsequent heat-treatment, Cu, Zn and Al distributed uniformly in the microstructure and a copper-based solid solution was formed. | ||
| کلیدواژهها | ||
| Accumulative roll bonding؛ Heat treatment؛ Multilayer؛ Solid solution | ||
| مراجع | ||
|
[1] Y. Saito, H. Utsunomiya, N. Tsuji, T. Sakai, Novel ultra-high straining process for bulk materials—development of the accumulative roll-bonding (ARB) process, Acta Materialia, 47 (1999) 579-583.
[2] M. Alizadeh, M.H. Paydar, Fabrication of Al/SiCP composite strips by repeated roll-bonding (RRB) process, Journal of Alloys and Compounds, 477 (2009) 811-816.
[3] A. Yazdani, E. Salahinejad, Evolution of reinforcement distribution in Al–B4C composites during accumulative roll bonding, Materials & Design, 32 (2011) 3137-3142.
[4] R. Jamaati, M.R. Toroghinejad, J. Dutkiewicz, J.A. Szpunar, Investigation of nanostructured Al/Al2O3 composite produced by accumulative roll bonding process, Materials & Design, 35 (2012) 37-42.
[5] M. Alizadeh, H.A. beni, M. Ghaffari, R. Amini, Properties of high specific strength Al–4wt.% Al2O3/B4C nano-composite produced by accumulative roll bonding process, Materials & Design, 50 (2013) 427-432.
[6] C.Y. Liu, Q. Wang, Y.Z. Jia, B. Zhang, R. Jing, M.Z. Ma, Q. Jing, R.P. Liu, Evaluation of mechanical properties of 1060-Al reinforced with WC particles via warm accumulative roll bonding process, Materials & Design, 43 (2013) 367-372.
[7] A. Ahmadi, M.R. Toroghinejad, A. Najafizadeh, Evaluation of microstructure and mechanical properties of Al/Al2O3/SiC hybrid composite fabricated by accumulative roll bonding process, Materials & Design, 53 (2014) 13-19.
[8] M. Reihanian, E. Bagherpour, M.H. Paydar, Particle distribution in metal matrix composites fabricated by accumulative roll bonding, Materials Science and Technology, 28 (2012) 103-108.
[9] M. Reihanian, E. Bagherpour, M.H. Paydar, On the achievement of uniform particle distribution in metal matrix composites fabricated by accumulative roll bonding, Materials Letters, 91 (2013) 59-62.
[10] J.-M. Lee, B.-R. Lee, S.-B. Kang, Control of layer continuity in metallic multilayers produced by deformation synthesis method, Materials Science and Engineering: A, 406 (2005) 95-101.
[11] G. Min, J.-M. Lee, S.-B. Kang, H.-W. Kim, Evolution of microstructure for multilayered Al/Ni composites by accumulative roll bonding process, Materials Letters, 60 (2006) 3255-3259.
[12] M.C. Chen, H.C. Hsieh, W. Wu, The evolution of microstructures and mechanical properties during accumulative roll bonding of Al/Mg composite, Journal of Alloys and Compounds, 416 (2006) 169-172.
[13] R.N. Dehsorkhi, F. Qods, M. Tajally, Investigation on microstructure and mechanical properties of Al–Zn composite during accumulative roll bonding (ARB) process, Materials Science and Engineering: A, 530 (2011) 63-72.
[14] A. Mozaffari, H. Danesh Manesh, K. Janghorban, Evaluation of mechanical properties and structure of multilayered Al/Ni composites produced by accumulative roll bonding (ARB) process, Journal of Alloys and Compounds, 489 (2010) 103-109.
[15] M. Eizadjou, A. Kazemi Talachi, H. Danesh Manesh, H. Shakur Shahabi, K. Janghorban, Investigation of structure and mechanical properties of multi-layered Al/Cu composite produced by accumulative roll bonding (ARB) process, Composites Science and Technology, 68 (2008) 2003-2009.
[16] M.R. Toroghinejad, R. Jamaati, J. Dutkiewicz, J.A. Szpunar, Investigation of nanostructured aluminum/copper composite produced by accumulative roll bonding and folding process, Materials & Design, 51 (2013) 274-279.
[17] L. Ghalandari, M.M. Moshksar, High-strength and high-conductive Cu/Ag multilayer produced by ARB, Journal of Alloys and Compounds, 506 (2010) 172-178.
[18] M. Tayyebi, B. Eghbali, Study on the microstructure and mechanical properties of multilayer Cu/Ni composite processed by accumulative roll bonding, Materials Science and Engineering: A, 559 (2013) 759-764.
[19] S. Roy, B.R. Nataraj, S. Suwas, S. Kumar, K. Chattopadhyay, Accumulative roll bonding of aluminum alloys 2219/5086 laminates: Microstructural evolution and tensile properties, Materials & Design, 36 (2012) 529-539.
[20] L. Ghalandari, M.M. Mahdavian, M. Reihanian, Microstructure evolution and mechanical properties of Cu/Zn multilayer processed by accumulative roll bonding (ARB), Materials Science and Engineering: A, 593 (2014) 145-152.
[21] A. Shabani, M.R. Toroghinejad, A. Shafyei, Fabrication of Al/Ni/Cu composite by accumulative roll bonding and electroplating processes and investigation of its microstructure and mechanical properties, Materials Science and Engineering: A, 558 (2012) 386-393.
[22] M.M. Mahdavian, L. Ghalandari, M. Reihanian, Accumulative roll bonding of multilayered Cu/Zn/Al: An evaluation of microstructure and mechanical properties, Materials Science and Engineering: A, 579 (2013) 99-107.
[23] F. C. Lovey, V. Torra, Shape memory in Cu-based alloys: phenomenological behavior at the mesoscale level and interaction of martensitic transformation with structural defects in Cu-Zn-Al, Progress in Materials Science, 44 (1999) 189-289.
[24] A. V. Traleski, S. Vurobi Jr, O.M. Cintho, Processing of Cu-Al-Ni and Cu-Zn-Al alloys by mechanical alloying, Materials Science Forum, 727-728 (2012) 200-205.
[25] X.X. Wu, X.Y. San, Y.L. Gong, L.P. Chen, C.J. Li, X.K. Zhu, Studies on strength and ductility of Cu–Zn alloys by stress relaxation, Materials & Design, 47 (2013) 295-299.
[26] K. Wu, H. Chang, E. Maawad, W.M. Gan, H.G. Brokmeier, M.Y. Zheng, Microstructure and mechanical properties of the Mg/Al laminated composite fabricated by accumulative roll bonding (ARB), Materials Science and Engineering: A, 527 (2010) 3073-3078.
[27] A. Mozaffari, M. Hosseini, H.D. Manesh, Al/Ni metal intermetallic composite produced by accumulative roll bonding and reaction annealing, Journal of Alloys and Compounds, 509 (2011) 9938-9945.
[28] H. Chang, M.Y. Zheng, C. Xu, G.D. Fan, H.G. Brokmeier, K. Wu, Microstructure and mechanical properties of the Mg/Al multilayer fabricated by accumulative roll bonding (ARB) at ambient temperature, Materials Science and Engineering: A, 543 (2012) 249-256.
[29] D. Askeland, P. Fulay, Essentials of Materials Science & Engineering, second ed., Cengage Learning, USA, 2008.
[30] C. Suryanarayana, Mechanical alloying and milling, Progress in Materials Science, 46 (2001) 1-184. | ||
|
آمار تعداد مشاهده مقاله: 3,937 تعداد دریافت فایل اصل مقاله: 2,192 |
||