. (1390). Degradation and cyclic crack resistance of continuous casting machine roll material under operating temperatures. , 35(2), 159-165. doi: 10.22099/ijstm.2011.903
. "Degradation and cyclic crack resistance of continuous casting machine roll material under operating temperatures". , 35, 2, 1390, 159-165. doi: 10.22099/ijstm.2011.903
. (1390). 'Degradation and cyclic crack resistance of continuous casting machine roll material under operating temperatures', , 35(2), pp. 159-165. doi: 10.22099/ijstm.2011.903
. Degradation and cyclic crack resistance of continuous casting machine roll material under operating temperatures. , 1390; 35(2): 159-165. doi: 10.22099/ijstm.2011.903

Degradation and cyclic crack resistance of continuous casting machine roll material under operating temperatures

Iranian Journal of Science and Technology Transactions of Mechanical Engineering
شناسنامه علمی شماره، دوره 35، شماره 2، فروردین 2011، صفحه 159-165    اصل مقاله (2.64 M)
شناسه دیجیتال (DOI): 10.22099/ijstm.2011.903
چکیده
The in-service cracks of the continuous casting machine roll are studied. The effects of high temperature fatigue crack growth were investigated for 25Kh1M1F steel, which is widely used for continuous casting rolls. In general, fatigue crack growth rates increased with increasing temperatures. At high crack growth rates, crack-tip plasticity was significant and propagation proceeded by ductile striation formation processes.         
 
کلیدواژه‌ها
Defects؛ fatigue crack growth؛ fractography؛ high temperature fatigue