Nanotwins Formation in Accumulative Roll-Bonded Brass | ||
| Iranian Journal of Materials Forming | ||
| مقاله 3، دوره 4، شماره 1، تیر 2017، صفحه 21-27 اصل مقاله (1.07 M) | ||
| نوع مقاله: Research Paper | ||
| شناسه دیجیتال (DOI): 10.22099/ijmf.2017.3945 | ||
| نویسندگان | ||
| S. Pasebani1؛ M. R. Toroghinejad* 2؛ G. Dini3 | ||
| 1School of Mechanical, Industrial, and Manufacturing Engineering Oregon State University Corvallis, OR 97331-6001 USA | ||
| 2Department of Materials Engineering, Isfahan University of Technology, Isfahan | ||
| 3Isfahan University | ||
| چکیده | ||
| Accumulative roll-bonding (ARB) is a severe plastic deformation process that is using rolling to produce ultrafine grains in coarse grained metallic materials. In this study, ARB has been applied on 70/30 brass up to 6 cycles at ambient temperature and non-lubricated conditions to apply a true strain up to 4.8 Von Mises strain. Microstructures of ARBed brass samples were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicated that during ARB cycles, the grain size decreased from micron-size to nano-size and mechanical twins were widely observed throughout the microstructure after cycle 1. However after cycle 3, the twinning activity became significantly limited and deformation occurred via shear bands formation. After cycle 6, the measured average grain size was about 50 nm and nanotwins were observed originating from grain boundaries and gain boundary junctions. With the reduction in the grain size down to nanometer, the pole mechanism was not the dominant mechanism of nanotwin formation and nanotwins were mainly produced via partial dislocation emission from grain boundaries and grain boundary junctions. | ||
| کلیدواژهها | ||
| Accumulative roll-bonding؛ nanotwins؛ nanostructured؛ 70/30 brass | ||
| مراجع | ||
|
[1] Y. H. Zhao, X. Z. Liao, Z. Horita, T. G. Langdon and Y. T. Zhu, Mat. Sci. Eng. A. 493 (2008) 123-129.
[2] J. A. Venables, Philos. Mags. 6 (1961) 379-396.
[3] C.X. Huang, K. Wang, S. D. Wu, Z. F. Zhang, G. Y. Li and S .X. Li, Acta. Mater. 54 (2006) 655-665.
[4] V. Yamakov, D. Wolf, S. R. Phillpot, A. K. Mukherjee and H. Gleiter, Nature. Mater. 1(2002) 45-48.
[5] J. Schiotz and K. W. Jacobsen, Science 301 (2003) 1357-1359.
[6] H. V. Swygenhoven, Science 296 (2002) 66-67.
[7] N. Tsuji, Y. Saito, S. H. Lee and Y. Minamino, Adv. Eng. Mat. 5(2003) 338-344.
[8] W. Wang, Y. B. Wang, X. Z. Liao , Y. H. Zhao, E. J. Lavernia, Y. T. Zhu, Z. Horita and T. G Langdon, Scripta. Mater. 60 (2009) 52-55.
[9] B. J. Duggan, M. Hatherly, W. B. Hutchinson and P. T. Wakefield, Metal. Science. 12 (1978) 343-350.
[10] G.H. Xiao, N. R. Tao and K. Lu, Mat. Sci. Eng. A. 513-514 (2009) 13-21.
[11] F.J. Humphreys and M. Hatherly, Recrystallization and related annealing phenomena, second ed, Elsevier Science Ltd, United Kingdom, 2004.
[12] Z. Horita, D. J. Smith, M. Nemoto, R. Z. Valiev and T. G. Langdon, J. Mater. Res. 13(1998) 446-449.
[13] X. Z. Liao, Y. H. Zhao, S. G. Srinivasan, Y. T. Zhu, R. Z. Valiev and D. V. Gunderov, Appl. Phys. Lett. 84(2004) 592-594.
[14] J. Cai, S. Shekhar, J. Wang and M. Ravi Shankar, Scripta Mater. 60(2009) 599-602.
[15] X. Z. Liao, Y. H. Zhao, Y. T. Zhu, R. Z. Valiev and D. V. Gunderov, J. Appl. Phys. 96(2004) 636-640.
[16] V. Yamakov, D. Wolf, S. R. Phillpot, A. K. Mukherjee and H. Gleiter, Nature. Mater. 3(2004) 43-47.
[17] H. V. Swygenhoven, M. Spacer and A. Caro, Acta. Mater. 47 (1999) 3117-3126.
[18] X. Z. Liao, F. Zhou, E. J. Lavernia, S. G. Srinivasan, M. I. Baskes, D. W. He and Y. T. Zhu, Appl. Phys. Lett. 83 (2003) 632- 634.
[19] X. Z. Liao, F. Zhou, E. J. Lavernia, D. W. He and Y.T. Zhu, Appl. Phys. Lett. 83 (2003) 5062-5064.
[20] X. Wu, Y. T. Zhu and E. Ma, Appl. Phys. Lett. 88 (2006) 121905- 121907.
[21] X. L. Wu and Y. T. Zhu, Appl. Phys. Lett. 89 (2006) 03192-03194.
[22] E. Ma, Y. M. Wang, Q. H. Lu, M. L. Sui, L. Lu and K. Lu, Appl. Phys. Lett. 85 (2004) 4932-4934.
[23] L. Lu, R. Schwaiger, Z. W. Shan, M. Dao, K. Lu and S. Suresh, Acta. Mater. 53 (2005) 2169- 2179. | ||
|
آمار تعداد مشاهده مقاله: 1,338 تعداد دریافت فایل اصل مقاله: 1,365 |
||