Effect of the Particle Size on the Deformation and Fracture Behavior of Al/4vol.%Al2O3 Composite Produced by Accumulative Roll Bonding (ARB) | ||
| Iranian Journal of Materials Forming | ||
| مقاله 2، دوره 2، شماره 2، دی 2015، صفحه 14-26 اصل مقاله (1.31 M) | ||
| نوع مقاله: Research Paper | ||
| شناسه دیجیتال (DOI): 10.22099/ijmf.2015.3237 | ||
| نویسندگان | ||
| M. Reihanian* 1؛ M. Naseri2؛ M. Jalili Shahmansouri2 | ||
| 1Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University, Ahvaz, Iran | ||
| 2Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran | ||
| چکیده | ||
| In this study, Al/Al2O3 composites with two different particle sizes of 1 µm and 0.3 µm were produced via accumulative roll bonding (ARB). The microstructure evolution, mechanical properties and fracture behavior of the composites were investigated. Results show that higher ARB cycles are required to achieve a uniform distribution of particles in the composite with 0.3 µm particle size. During ARB, dense cluster of the particles broke up and a uniform distribution of particles was achieved after eight ARB cycles. The tensile strength of the composite with 1 µm and 0.3 µm particle size enhanced by increasing the number of ARB cycles, reached to about 170 MPa and 175 MPa, respectively, in comparison to that of the annealed Al (about 47 MPa). The finer particles caused a higher tensile strength due to the decrease in the distance between the particles at a given volume fraction. The fracture surface of both composites revealed ductile type fracture characterized by dimples. The dimples in the composite with particle size of 1 μm were larger and deeper. | ||
| کلیدواژهها | ||
| accumulative roll bonding (ARB)؛ Metal matrix composites (MMCs)؛ Microstructure؛ Mechanical properties | ||
| مراجع | ||
|
[1] D.B. Miracle, Metal matrix composites–From science to technological significance, Composites Science and Technology, 65(2005) 2526-2540. [2] D.J. Lloyd, Particle reinforced aluminium and magnesium matrix composites, International Materials Reviews, 39(1994) 1-23.
[3] G. O'Donnell and L. Looney, Production of aluminium matrix composite components using conventional PM technology, Materials Science and Engineering: A, 303(2001) 292-301.
[4] J. Hashim, L. Looney and M.S.J. Hashmi, Metal matrix composites: production by the stir casting method, Journal of Materials Processing Technology, 92–93(1999) 1-7.
[5] M. Alizadeh and M.H. Paydar, Fabrication of nanostructure Al/SiCP composite by accumulative roll-bonding (ARB) process, Journal of Alloys and Compounds, 492 (2010) 231-235.
[6] R. Jamaati and M.R. Toroghinejad, Application of ARB process for manufacturing high-strength, finely dispersed and highly uniform Cu/Al2O3 composite, Materials Science and Engineering: A, 527(2010) 7430-7435.
[7] M. Reihanian, F.K. Hadadian and M.H. Paydar, Fabrication of Al–2vol% Al2O3/SiC hybrid composite via accumulative roll bonding (ARB): An investigation of the microstructure and mechanical properties, Materials Science and Engineering: A, 607(2014) 188-196.
[8] R. Jamaati, M.R. Toroghinejad and H. Edris, Effect of SiC nanoparticles on the mechanical properties of steel-based nanocomposite produced by accumulative roll bonding process, Materials and Design, 54(2014) 168-173.
[9] Y. Saito, H. Utsunomiya, N. Tsuji and T. Sakai, Novel ultra-high straining process for bulk materials—development of the accumulative roll-bonding (ARB) process, Acta Materialia, 47 (1999) 579-583.
[10] B.L. Li, N. Tsuji and N. Kamikawa, Microstructure homogeneity in various metallic materials heavily deformed by accumulative roll-bonding, Materials Science and Engineering: A, 423 (2006) 331-342.
[11] R. Jamaati and M.R. Toroghinejad, Manufacturing of high-strength aluminum/alumina composite by accumulative roll bonding, Materials Science and Engineering: A, 527(2010) 4146-4151.
[12] M. Rezayat, A. Akbarzadeh and A. Owhadi, Production of high strength Al–Al2O3 composite by accumulative roll bonding, Composites Part A: Applied Science and Manufacturing, 43 (2012) 261-267.
[13] R. Jamaati, S. Amirkhanlou, M.R. Toroghinejad and B. Niroumand, Effect of particle size on microstructure and mechanical properties of composites produced by ARB process, Materials Science and Engineering: A, 528(2011) 2143-2148.
[14] M. Karbalaei Akbari, H.R. Baharvandi and K. Shirvanimoghaddam, Tensile and fracture behavior of nano/micro TiB2 particle reinforced casting A356 aluminum alloy composites, Materials and Design, 66(2015) 50-161.
[15] M. Alizadeh & M.H. Paydar, Fabrication of Al/SiCP composite strips by repeated roll-bonding (RRB) process, Journal of Alloys and Compounds, 477(2009) 811-816.
[16] M. Alizadeh, Comparison of nanostructured Al/B4C composite produced by ARB and Al/B4C composite produced by RRB process, Materials Science and Engineering: A, 528(2010) 578-582.
[17] A. Yazdani, E. Salahinejad, J. Moradgholi and M. Hosseini, A new consideration on reinforcement distribution in the different planes of nanostructured metal matrix composite sheets prepared by accumulative roll bonding (ARB), Journal of Alloys and Compounds, 509 (2011) 9562-9564.
[18] L. Li, K. Nagai and F. Yin, Progress in cold roll bonding of metals, Science and Technology of Advanced Materials, 9(2008) 023001. [19] M. Alizadeh and M.H. Paydar, High-strength nanostructured Al/B4C composite processed by cross-roll accumulative roll bonding, Materials Science and Engineering: A, 538(2012) 14-19.
[20] M. Reihanian, E. Bagherpour and M.H. Paydar, On the achievement of uniform particle distribution in metal matrix composites fabricated by accumulative roll bonding, Materials Letters, 91(2013) 59-62.
[21] M. Alizadeh, H.A. beni, M. Ghaffari and R. Amini, Properties of high specific strength Al–4wt.% Al2O3/B4C nano-composite produced by accumulative roll bonding process, Materials and Design, 50(2013) 427-432.
[22] M. Rezayat, A. Akbarzadeh and A. Owhadi, Fabrication of high-strength Al/SiCp nanocomposite sheets by accumulative roll bonding, Metall and Mat Trans A, 43(2012) 2085-2093.
[23] M. Reihanian, R. Ebrahimi, N. Tsuji and M.M. Moshksar, Analysis of the mechanical properties and deformation behavior of nanostructured commercially pure Al processed by equal channel angular pressing (ECAP), Materials Science and Engineering: A, 473(2008) 189-194.
[24] M. Reihanian, R. Ebrahimi, M.M. Moshksar, D. Terada and N. Tsuji, Microstructure quantification and correlation with flow stress of ultrafine grained commercially pure Al fabricated by equal channel angular pressing (ECAP), Materials Characterization, 59(2008) 1312-1323.
[25] T.H. Courtney, Mechanical behavior of materials, 2nd edition, Waveland Press, Inc., 2005.
[26] H. Sekine and R. Chent, A combined microstructure strengthening analysis of SiCp/Al metal matrix composites, Composites, 26(1995) 183-188.
[27] M. Alizadeh, Strengthening mechanisms in particulate Al/B4C composites produced by repeated roll bonding process, Journal of Alloys and Compounds, 509(2011) 2243-2247.
[28] A. Azushima, R. Kopp, A. Korhonen, D.Y. Yang, F. Micari, G.D. Lahoti, P. Groche, J. Yanagimoto, N. Tsuji, A. Rosochowski and A. Yanagida, Severe plastic deformation (SPD) processes for metals, CIRP Annals - Manufacturing Technology, 57(2008) 716-735.
[29] M. Alizadeh and M. Talebian, Fabrication of Al/Cup composite by accumulative roll bonding process and investigation of mechanical properties, Materials Science and Engineering: A, 558(2012) 331-337.
[30] A. Ahmadi, M.R. Toroghinejad and A. Najafizadeh, Evaluation of microstructure and mechanical properties of Al/Al2O3/SiC hybrid composite fabricated by accumulative roll bonding process, Materials and Design, 53(2014) 13-19.
[31] M.A. Meyers and K.K. Chawla, Mechanical Behavior of Materials, 2nd edition, Cambridge University Press, UK, (2009).
[32] D.J. Wulpi, Understanding how Components Fail, 3rd edition, ASM International, USA, (2013). | ||
|
آمار تعداد مشاهده مقاله: 2,902 تعداد دریافت فایل اصل مقاله: 2,542 |
||