Study of the Thermally Stimulated Depolarization Current (TSDC) for composites of Acrylonitrile Butadiene Rubber (NBR) loaded with HAF | ||
| Iranian Journal of Science | ||
| مقاله 15، دوره 37، شماره 3، آبان 2013، صفحه 313-318 اصل مقاله (437.97 K) | ||
| نوع مقاله: Regular Paper | ||
| شناسه دیجیتال (DOI): 10.22099/ijsts.2013.1609 | ||
| نویسندگان | ||
| M. Amin1؛ G. M. Nasr1؛ K. M. El-Shokrofy2؛ Sh. A. Mansour* 3 | ||
| 1Physics Department, Faculty of Science, Cairo University, Cairo, Egypt | ||
| 2Basic Engineering Science Department, Faculty of Engineering, Menofia University, Shebin El-Kom, Egypt | ||
| 3Cairo University | ||
| چکیده | ||
| The thermally stimulated discharge (TSDC) current is studied for acrylonitrile butadiene rubber (NBR) loaded with different high abrasion furnace carbon black (HAF). TSDC peak appears only for higher HAF contents > 60phr (70 and 80phr of HAF contents), the TSDC spectra consist of a sharp peak corresponding to a peak temperature Tm which is slightly shifted to higher temperature for 70phr loaded NBR samples and to lower temperature for 80phr loaded NBR sample, with poling field (10V/cm to 50V/cm). The activation energy U and relaxation time for TSDC peak were calculated using the initial rise method. The calculated values of U are nearly constant for sample 70phr and slightly increase for sample 80phr with increasing poling field Ep . The calculated values of at peak temperature Tm are nearly constant for two samples (70phr & 80phr) with different poling field, whereas the calculated values of relaxation time at To = 300K increased with increase of poling field. | ||
| کلیدواژهها | ||
| Conductive elastomers TSDC؛ acrylonitrile butadiene rubber (NBR)؛ HAF | ||
|